進口高壓合金管的標準 美標16mn無縫鋼管介紹
執行標準
GB6479——化肥設備用高壓無縫鋼管
GB9948——石油裂化用無縫鋼管
ASTM A213 ——Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes
ASTM A335 ——Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service
JIS G3458 ——Alloy Steel Pipes (STPA 12/ 20/ 22/ 23/ 24/ 25/ 26)
JIS G3462 ——Alloy Steel for Boiler and Heat Exchanger Tubes (STBA12/ 13/ 20/ 22)
JIS G3467 ——Steel Tubes for Fired Heater (STF 410/STFA 12/ 22/ 23/ 24/ 25/ 26)
DIN17175-79Ⅲ——Electrical Resistance Or Induction Welded Steel Tubes for Elevated Temperature
主要生產無縫鋼管牌號
Cr5Mo (STFA25 STPA25 STBA25 T5 P5)
15CrMo (STFA22 STPA22 STBA22 T12 P12)
1.25Cr0.5Mo (STFA23 STPA23 STBA23 T11 P11)
Cr9Mo (STFA26 STPA26 STBA26 T9 P9)
12Cr1MoV
12Cr2Mo (10CrMo910 T22 P22)
10Cr9Mo1VNb T91 (P91)
12Cr2MoWVTiB (R102)
尺寸公差
查表
力學性能
|
牌號 |
常溫力學性能 |
|
標準號 |
鋼號 |
σs(MPa) |
σb(MPa) |
δs(%) |
αk(J/cm2) |
|
GB5310 |
12CrMo |
206 |
412-559 |
21 |
69u |
|
15CrMo |
235 |
441-638 |
21 |
59u |
|
12Cr1MoV |
255 |
471-638 |
21 |
59u |
|
12Cr2Mo |
280 |
450-600 |
20 |
|
|
ASTM A335 |
P1 |
207 |
379 |
22 |
|
|
P11 |
207 |
413 |
22 |
|
|
P12 |
207 |
413 |
22 |
|
|
P2 |
207 |
379 |
22 |
|
|
P22 |
207 |
413 |
22 |
|
|
P5 |
207 |
413 |
22 |
|
|
P9 |
207 |
413 |
22 |
|
|
DIN17175 |
19Mn5 |
300-310 |
510-610 |
19 |
|
|
13CrMo44 |
280-290 |
440-590 |
22 |
|
|
14MoV63 |
310-319 |
460-610 |
20 |
|
|
10CrMo910 |
269-280 |
450-600 |
|
|
|
JIS G3458 |
STPA12 |
206 |
382 |
|
|
|
STPA20 |
206 |
412 |
|
|
|
STPA22 |
206 |
412 |
|
|
|
STPA23 |
206 |
412 |
|
|
|
STPA24 |
206 |
412 |
|
|
|
STPA25 |
206 |
412 |
|
|
|
STPA26 |
206 |
412 |
|
|
|
JIS G3462 |
STBA12 |
206 |
382 |
|
|
|
STBA13 |
206 |
412 |
|
|
|
STBA22 |
206 |
412 |
|
|
|
STBA20 |
206 |
412 |
|
|
|
STBA23 |
206 |
412 |
|
|
化學成分
|
牌號 |
化學成分(%) |
|
標準號 |
鋼號 |
C |
Mn |
Si |
Cr |
Mo |
V |
S |
P |
|
GB5310 |
12CrMo |
0.08-0.15 |
0.40-0.70 |
0.17-0.37 |
0.40-0.70 |
0.40-0.55 |
|
≤0.035 |
≤0.035 |
|
15CrMo |
0.12-0.18 |
0.40-0.70 |
0.17-0.37 |
0.80-1.10 |
0.40-0.55 |
|
≤0.035 |
≤0.035 |
|
12Cr1MoV |
0.08-0.15 |
0.40-0.70 |
0.17-0.37 |
0.90-1.20 |
0.25-0.35 |
0.15-0.30 |
≤0.035 |
≤0.035 |
|
12Cr2Mo |
0.08-0.15 |
0.40-0.70 |
≤0.50 |
2.00-2.50 |
0.90-1.20 |
|
≤0.035 |
≤0.035 |
|
ASTM A335 |
P1 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P11 |
≤0.15 |
0.30-0.60 |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
≤0.030 |
≤0.030 |
|
P12 |
≤0.15 |
0.30-0.61 |
≤0.50 |
0.80-1.25 |
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P2 |
0.10-0.20 |
0.30-0.61 |
0.10-0.30 |
0.50-0.81 |
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
1.90-2.60 |
0.87-1.13 |
|
≤0.030 |
≤0.030 |
|
P5 |
≤0.15 |
0.30-0.60 |
≤0.50 |
4.00-6.00 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
P9 |
≤0.15 |
0.30-0.60 |
0.25-1.00 |
8.00-10.00 |
0.90-1.10 |
|
≤0.030 |
≤0.030 |
|
DIN17175 |
19Mn5 |
0.17-0.22 |
1.00-1.30 |
0.30-0.60 |
≤0.30 |
|
|
≤0.04 |
≤0.04 |
|
13CrMo44 |
0.10-0.18 |
0.40-0.70 |
0.10-0.35 |
0.70-1.10 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
14MoV63 |
0.10-0.18 |
0.40-0.70 |
0.10-0.35 |
0.30-0.60 |
0.50-0.70 |
0.22-0.32 |
≤0.035 |
≤0.035 |
|
10CrMo910 |
0.08-0.15 |
0.40-0.70 |
≤0.50 |
2.00-2.50 |
0.90-1.20 |
|
≤0.035 |
≤0.035 |
|
JIS G3458 |
STPA12 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA20 |
0.10-0.20 |
0.30-0.60 |
0.10-0.50 |
0.50-0.80 |
0.40-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA23 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
STPA24 |
≤0.15 |
0.30-0.60 |
≤0.50 |
1.90-2.60 |
0.87-1.13 |
|
≤0.030 |
≤0.030 |
|
STPA25 |
≤0.15 |
0.30-0.60 |
≤0.50 |
4.00-6.00 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
STPA26 |
≤0.15 |
0.30-0.60 |
0.25-1.00 |
8.00-10.00 |
0.90-1.10 |
|
≤0.030 |
≤0.030 |
|
JIS G3462 |
STBA12 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA13 |
0.15-0.25 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA20 |
0.10-0.20 |
0.30-0.60 |
0.10-0.50 |
0.50-0.80 |
0.40-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA23 |
≤0.15 |
0.30-0.60 |
0.50-1.00 |
1.00-1.50 |
0.45-0.65 |
|
|
|
進口高壓合金管的標準 美標16mn無縫鋼管介紹
16Mn低合金管
16Mn合金管
16Mn叫低合金高強度結構鋼
低合金高強度結構鋼：含碳量為0.1%-0.25%,加入主要合金元素錳、硅、釩、鈮和鈦等；它的含合金總量<3%。按強度分為300、350、400和450MPa等4個級別。主要有Q295、Q345、Q390、Q420、Q460�！癚”是屈服的“屈”字的漢語拼音大寫字頭，其后數字為該牌號最小屈服點(σs)值，其后的符號是按照該鋼雜質元素(硫、磷)含量由高到低并伴隨碳、錳元素的變化而分為A、B、C、D四等。其中A、B級鋼通常稱16Mn。
化學成分：C：0.12-0.20；Mn：1.20-1.60；Si：0.20-0.55；
抗拉強度：470-660牛/平方毫米；
屈服強度：275-345牛/平方毫米；
伸長率：21%。具體值要根據鋼材的厚度或直徑，以上數據對應鋼材的厚度或直徑為：16-100mm
用途：用于橋梁的專用鋼種為“16Mnq”，汽車大梁的專用鋼種為“16MnL”，壓力容器的專用鋼種為“16MnR”。
16Mn
16Mn是鋼材的一種材質。16Mn是過去的叫法，現在的稱為：Q345
16：代表這種鋼材中碳的含量在0.16%左右。
Mn：單獨提出來,是因為五大元素(碳C，硅Si，錳Mn，磷P，硫S)中,錳的含量高,大約在1.20-1.60%左右。
16Mn屬低合金鋼板系列，在此系列中，為最普通材質，或者牌號的鋼板。
根據特殊的要求，可以對鋼板進行一些特殊的處理：熱處理和Z向性能。
◆ 熱處理：控軋，正火等等。
◆ Z向性能：Z15，Z25，Z35
主要特性：
綜合性能好，低溫性能好，泠沖壓性能，焊接性能和可切削性能好。
應用舉例：
礦山，運輸，化工等各種機械。
16Mn化學成分及力學性能
16Mn化學成分
|
牌號 |
化學成分(質量分數)(%) |
|
C |
Si |
Mn |
P≤ |
S≤ |
Cr |
Mo |
V |
|
16Mn |
0.12-0.20 |
0.20-0.60 |
1.20-1.60 |
0.030 |
0.030 |
- |
- |
- |
16Mn力學性能
|
牌號 |
拉力強度MPa |
屈服點MPa |
伸長率(%) |
|
16Mn |
490-670 |
320 |
21 |
16Mn鍛件的化學成分
|
牌號 |
化學成分(質量分數)(%) |
|
C
≤ |
Si
≤ |
Mn |
P
≤ |
S
≤ |
Nb |
Ti |
V |
|
Q345(16Mn)
低合金高強度結構鋼 |
0.20% |
0.55% |
1.00%-1.60 |
0.045% |
0.045% |
0.015%-0.060% |
0.02%-0.20% |
0.02%-0.15% |
16Mn鍛件的力學性能：
|
公稱壁厚 |
熱處理狀態 |
拉伸試驗σb |
沖擊試驗 |
硬度試驗HB |
物理性質 |
應用舉例 |
|
≤300 mm |
正火，
正火+回火
回火溫度℃≥600 |
450-600 MPa；
σs≥275 MPa；
δ5≥20% |
試驗溫度0℃；
Akv ,
J≥31 |
121-178 |
綜合力學性能好，焊接
性、冷、熱加工性能和耐
蝕性能均好，C、D、E
級鋼具有良好的低溫韌
性。 |
船舶，鍋爐，壓
力容器，石油儲
罐，橋梁，電站
設備。起重運輸
機械及其他較高
載荷的焊接結構
件。 |
|